Paramagnetic Mn₈Fe₄-co-Polystyrene Nanobeads as a Potential T₁-T₂ Multimodal Magnetic Resonance Imaging Contrast...

In developing a cluster-nanocarrier design, as a magnetic resonance imaging contrast agent, we have investigated the enhanced relaxivity of a manganese and iron-oxo cluster grafted within a porous polystyrene nanobead with increased relaxivity due to a higher surface area. The synthesis of the cluster-nanocarrier for the cluster Mn₈Fe₄O₁₂(O₂CC₆H₄CH═CH₂)₁₆(H₂O)₄, cross-linked with polystyrene (the nanocarrier), under miniemulsion conditions is described. By including a branched hydrophobe, iso-octane, the resulting nanobeads are porous and ∼70 nm in diameter. The increased surface area of the nanobeads compared to nonporous nanobeads leads to an enhancement in relaxivity; r₁ increases from 3.8 to 5.2 ± 0.1 mM^-1 s^-1, and r₂ increases from 11.9 to 50.1 ± 4.8 mM^-1 s^-1, at 9.4 teslas, strengthening the potential for T₁ and T₂ imaging. Several metrics were used to assess stability, and the porosity produced no reduction in metal stability. Synchrotron X-ray fluorescence microscopy was used to demonstrate that the nanobeads remain intact in vivo. In depth, physicochemical characteristics were determined, including extensive pharmacokinetics, in vivo imaging, and systemic biodistribution analysis.