From Unimolecular Template to Silver Nanocrystal Clusters: An Effective Strategy to Balance Antibacterial Activity...

Silver nanomaterials have attracted a great deal of interest due to their broad-spectrum antimicrobial activity. However, it is still challenging to balance the high antibacterial efficiency with low damage to biological cells of silver nanostructures, especially when the diameter decreases to less than 10 nm. Here, we developed a new type of Ag nanohybrid material via a unimolecular micelle template method, which presents amazing antibacterial activities and almost noncytotoxicity. First, water-soluble multiarm star-shaped brushlike copolymer α-CD-g-[(PEO₄₀-g-PAA₅₀)-b-PEO₅]₁₈ was precisely synthesized and its micelle behavior in different solvents was revealed. Then, nanocrystal clusters assembled by Ag grains (Ag@Template NCs) were prepared through an in situ redox route using the unimolecular micelle of α-CD-g-[(PEO₄₀-g-PAA₅₀)-b-PEO₅]₁₈ as the soft template, AgNO₃ as a precursor, and tetrabutylammonium borohydride (TBAB) as the reducing agent. The overall size of the achieved Ag@Template NCs is controlled by the template structure at around 40 nm (D_h in DMF), and the size of the Ag grain can be easily regulated from ∼1 to ∼5 nm by adjusting the feeding ratio of AgNO₃/acrylic acid (AA) units in the template from 1:10 to 1:1. Benefitting from the structural design of the template, all Ag@Template NCs prepared here exhibit excellent dispersibility and chemical stability in different aqueous environments (neutral, pH = 5.5, and 0.9% NaCl physiological saline solution), which play a crucial role in the long-term storage and potential application in a complex physiological environment. The antibacterial and cytotoxicity tests indicate that Ag@Template NCs display much better performance than Ag nanoparticles (Ag NPs), which have a comparable overall size of ∼25 nm. The inhibitory capability of Ag@Template NCs to bacteria strongly depends on the grain size. Specifically, the Ag@Template-1 NC assembled by the smallest grains (1.6 ± 0.3 nm) presents the best antibacterial activity. For E. coli (-), the MIC value is as low as 5 μg/mL (0.36 μg/mL of Ag), while for S. aureus (+), the value is around 10 μg/mL (0.72 μg/mL of Ag). The survival rate of L02 cells and lactate dehydrogenase assay together illustrate the low cytotoxicity possessed by the prepared Ag@Template NCs. Therefore, the proposed Ag@Template NC structure successfully resolves the high reactivity, instability, and fast oxidation issues of the ultrasmall Ag nanoparticles, and integrates high antibacterial efficiency and nontoxicity to biological cells into one platform, which implies its broad potential application in biomedicine.