Interfacial Conductivity Enhancement and Pore Confinement Conductivity-Lowering Behavior inside the Nanopores of...

Solid nanocomposite electrolytes (nano-SCEs) that exhibit higher ionic conductivity than the individual confined electrolyte were investigated for high-performance solid-state batteries. Understanding the behavior of Li-ion conduction through the pores is important to design ideal nanoporous structures for nano-SCEs, which are composed of an ionic liquid electrolyte (ILE) in a highly porous (∼90%) silica matrix. To establish the relationship between the pore structure of the silica matrix and the ionic conductivity of the solid nanocomposite, the liquid electrolyte fraction was successfully extracted from the nano-SCE to reveal the fragile porous silica matrix. A careful drying using the CO₂ supercritical drying method helps in sustaining the original structure, preventing its collapse due to surface tension. The pore size distribution, Brunauer-Emmett-Teller (BET) surface area, and porosity were characterized using scanning electron microscopy, transmission electron microscopy, and N₂ adsorption/desorption techniques. Our results revealed a wide size distribution of macropores and mesopores in the silica matrix. The pore size increased and the effective surface area decreased with increasing ILE/SiO₂ molar ratio. The interface conductivity enhancement was found to increase with the thickness of the adsorbed (ice-like) bound-water layer on the silica surface, confirming that the strong hydrogen bonding of the adsorbed ionic liquid molecules on the bound-water layer causes the conduction promotion effect in the nano-SCE. In addition, a large number of small pores lead to a severe pore confinement effect that results in a decreased conductivity due to the increasing viscosity of the ILE filling the pores. The conductivity can be improved by realizing a nano-SCE with an optimized pore size to minimize the pore confinement effect.