Mechanical characterization and neutrophil NETs response of a novel hybrid geometry polydioxanone near-field...

Near-field electrospinning (NFES) is a direct fiber writing sub-technique derived from traditional electrospinning (TES) by reducing the air gap distance to the magnitude of millimeters. In this paper, we demonstrate a NFES device designed from a commercial 3D printer to semi-stably write polydioxanone (PDO) microfibers. The print head was then programmed to translate in a stacking grid pattern, which resulted in a scaffold with highly aligned grid fibers that were intercalated with low density, random fibers. As the switching process can be considered random, increasing the grid size results in both a lower density of fibers in the center of each grid cell as well as a lower density of 'rebar-like' stacked fibers. These scaffolds resulted in tailorable as well as greater surface pore sizes as given by scanning electron micrographs and 3D permeability as indicated by fluorescent microsphere filtration compared to TES scaffolds of the same fiber diameter. Furthermore, ultimate tensile strength, percent elongation, yield stress, yield elongation, and Young's modulus were all tailorable compared to the static TES scaffold characterization. Lastly, the innate immune response of neutrophil extracellular traps was attenuated on NFES scaffolds compared to TES scaffolds. These results suggest that this novel NFES scaffold architecture of PDO can be highly tailored as a function of programming for a variety of biomedical and tissue engineering applications.