Improvement on properties of experimental resin cements containing an iodonium salt cured under challenging...

The use of resin cements in clinical practice entails photopolymerization through prosthetic devices, which precludes light penetration. The objective of this study was to modify experimental resin cements (ERCs) with diphenyliodonium hexafluorophosphate (DPI) in an attempt to improve chemical and mechanical properties of materials cured with reduced irradiance and final radiant exposure.

A co-monomer base containing a 1:1 mass ratio of 2.2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenyl]propane (bis-GMA) and triethyleneglycol dimethacrylate (TEGDMA) was prepared, with 1mol% of camphorquinone and 2mol% of ethyl 4-(dimethylamino)benzoate as initiator system. The resin was divided into 4 fractions according to the DPI concentrations (0, 0.5, 1 and 2mol%). The challenging polymerization condition was simulated performing the light activation (12, 23 and 46s) through a ceramic block (3mm thick). The irradiance was assessed with a calibrated spectrometer (1320mW/cm²), resulting in three levels of radiant exposure (0.58, 1.1 and 2.2J/cm²). The polymerization kinetics was evaluated in real-time using a spectrometer (Near-IR). Water sorption and solubility was analyzed and the cohesive strength of resins obtained through the microtensile test. Polymerization stress was assessed by Bioman method.

Resins containing DPI had higher degree of conversion and rate of polymerization than the control (without DPI). The use of DPI reduced water sorption and solubility, and led to higher cohesive strength compared to resins without the iodonium salt. However, the stress of polymerization was higher for experimental resins with DPI.

Even under remarkably reduced irradiance, cements containing a ternary initiating system with an iodonium salt can present an optimal degree of conversion and chemical/mechanical properties.