Pre-pyrolysis metal and base addition catalyzes pore development and improves organic micropollutant adsorption to...

Biochars were produced from pine feedstock pretreated with aqueous base, NaOH, at pH 9 and 11, and alkali and alkaline earth metals (AAEMs) Na, K, Ca, and Mg at 10^-3 and 1 M. The effects of base and AAEM feedstock pretreatment on biochar surface area, pore size distribution, and adsorption capacity of two organic micropollutants (OMPs), 2,4-dichlorophenoxyacetic acid and sulfamethoxazole, from surface water with background dissolved organic matter (DOM) were evaluated. Base pretreatment significantly increased surface area within micropores (<2 nm diameter). AAEM pretreatment caused pore widening, increasing surface area within pores >2 nm in diameter. The catalytic activity of AAEMs, assessed by generation of non-micropore surface area, decreased in the following order: Ca > K > Na > Mg. All pretreated biochars outperformed untreated biochar for OMP adsorption. Biochar pretreated by aqueous base at pH 11 showed over an order of magnitude increase in OMP adsorption, nearly matching the performance of commercial activated carbon. OMP adsorption from surface water was positively correlated with biochar micropore surface area and negatively correlated with non-micropore surface area, which was linked to higher levels of DOM competition. Base and AAEM pretreatment of biochar feedstocks can increase OMP adsorption for water treatment applications by tuning pore structure and surface area.