Enhancing the antifouling and rejection properties of PVDF membrane by Ag3PO4-GO modification
Gongduan Fan1, Chongguo Chen2, Xiaolei Chen2
1College of Civil Engineering, Fuzhou University, 350116, Fujian, China; State Key Laboratory of Photocatalysis on Energy and Environment, Fuzhou University, 350002, Fujian, China; Fujian Provincial Key Laboratory of Electrochemical Energy Storage Materials, Fuzhou University, 350002, Fujian, China.
Abstract:
Ultrafiltration is an environmentally friendly water treatment technology, but membrane fouling significantly impacts membrane performance and service life. Photocatalytic modification of membrane is regarded as an effective way for membrane fouling control. In this study, graphite oxide (GO), Ag3PO4 and Ag3PO4-GO nanomaterials were applied in polyvinylidene fluoride (PVDF) ultrafiltration membranes modification, and the membranes was denoted as P-GO, P-AgP and P-AgP@GO, respectively. Filtration of humic acid (HA) at different operating conditions was adopted in evaluation of membrane performance. Among them, P-AgP@GO had the best permeation, rejection and antifouling performances, and could maintain excellent properties when operation conditions (HA concentration, operation pressure, pH and ionic strength) were changed. Furthermore, the effect of photocatalysis on the self-cleaning performance and its mechanism were revealed. The overall performance of P-AgP@GO could be enhanced by visible light irradiation, and extending the visible illumination time during the filtration was conducive to the reusability.