Development of polyvinyl alcohol-based carbon nano fiber sheet for thermal interface material

Polyvinyl alcohol (PVA)-based carbon nanofiber (CNF) sheets are fabricated as an innovative thermal interface material (TIM), which is a potential substitute for traditional TIMs. Five types of PVA-based CNF sheets were fabricated at different mass ratios of PVA:vapor-grown carbon fiber (VGCF) (1:0.100, 1:0.070, 1:0.050, 1:0.030, 1:0.025). The thickness of the PVA-based CNF sheets was 30-50 µm, which was controlled by the amount of VGCF. The microstructure of the CNF sheets indicated that VGCFs were arranged in random directions inside the sheet, and PVA was formed as a membrane between two VGCFs. However, many pores were found to exist between the VGCFs. The porosity of the PVA-based CNF sheets decreased from 25 to 13% upon decreasing the mass ratio of VGCF from 43.38 to 16.13%. The density and Shore hardness of all CNF sheets were 1.03-1.15 × 10⁶ g m^-3 and 82.4-85.0 HS, respectively. The highest thermal conductivity, measured as the mass ratio of PVA:VGCF, was achieved at 1:0.05, with the in-plane thermal conductivity of the fabricated sheet being 14.3 W m^-1 k^-1.