Magnetization Reversal and Dynamics in Epitaxial Fe/Pt Spintronic Bilayers Stimulated by Interfacial Fe₃O₄...

We have explored the impact of elevated growth and annealing temperatures on the local interfacial structure of thin Fe(12 nm)/Pt(10 nm) spintronic bilayers, epitaxially grown on MgO (100), and their correlation to magnetization reversal and dynamics. Electron-beam evaporation growth and subsequent annealing at 450 °C causes significant roughening of the MgO/Fe interface with irregular steps and multilevel (100) MgO surface terraces. Consequently, threading dislocations emerging at the step edges propagated in the Fe layer and terminated at the Fe/Pt interface, which appears pitted with pits 1.5-3 nm deep on the Fe side. Most of the pits are filled with the overlying Pt, whereby others by ferrimagnetic Fe₃O₄, forming nanoparticles that occupy nearly 9% of the Fe/Pt interfacial area. Fe₃O₄ nanoparticles occur at the termination sites of threading dislocations at the Fe/Pt interface, and their population density is equivalent to the density of threading dislocations in the Fe layer. The morphology of the Fe/Fe₃O₄/Pt system has a strong impact on the magnetization reversal, enhancing the coercive field and inducing an exchange bias below 200 K. Furthermore, low-temperature spin pumping and inverse spin Hall effect voltage measurements reveal that below their blocking temperature the nanoparticles can influence the spin current transmission and the spin rectification effects.