Computing the Fatigue Life of Cold Spray Repairs to Simulated Corrosion Damage

Daren Peng1, Caixian Tang2, Neil Matthews2

  • 1Centre of Expertise in Structural Mechanics, Department of Mechanical and Aeronautical Engineering, Monash University, Wellington Rd, Clayton, VIC 3800, Australia.

Materials (Basel, Switzerland)
|August 27, 2021
PubMed

Keywords:
EZ-19-01MIL-STD-1530Dcold spray repairdurabilityskin corrosion

More Related Videos

Imaging Corrosion at the Metal-Paint Interface Using Time-of-Flight Secondary Ion Mass Spectrometry07:24

Imaging Corrosion at the Metal-Paint Interface Using Time-of-Flight Secondary Ion Mass Spectrometry

Published on: May 6, 2019

8.4K
Metal Corrosion and the Efficiency of Corrosion Inhibitors in Less Conductive Media10:05

Metal Corrosion and the Efficiency of Corrosion Inhibitors in Less Conductive Media

Published on: November 3, 2018

18.1K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
295
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
306
Frost Action on Concrete01:27

Frost Action on Concrete

Concrete structures in cold climates, such as those along roadsides, can retain moisture. This moisture makes them susceptible to frost-related damage when temperatures fall below freezing. Adding moisture worsens the damage during temperature fluctuations, leading to repeated freezing and thawing. De-icing salts, spread over these structures to melt ice, add to the freeze-thaw cycle, and draw even more moisture into the concrete.
This freeze-thaw cycle primarily causes surface scaling, where...
185