Effects of Sc and Zr Addition on Microstructure and Mechanical Properties of AA5182
Jingxiao Li1,2, Xiaofang Yang1,2, Shihua Xiang1,2
1Shenyang National Laboratory for Materials Science, Chongqing University, Chongqing 400044, China.
Abstract:
The effects of 0.1 wt.% Sc and 0.1 wt.% Zr addition in AA5182 on microstructure and mechanical properties were investigated. Results show that Al3(ScxZr1-x) dispersoids formed in AA5182. Observation of ingots microstructures showed that the grain size of 5182-Sc-Zr alloy was 56% lower than that of based AA5182. Isothermal annealing between 230 °C and 500 °C for 2 h was performed to study the recrystallization, tensile properties and dispersoid coarsening. The recrystallization was inhibited by the dispersoids, and the alloy microstructure remained deformed after annealing. Al3(ScxZr1-x) in AA5182 was stable when annealing below 400 °C, while parts of dispersoids coarsened significantly when heating at 500 °C. The addition of Sc and Zr allowed YS of 5182 alloy to achieve 247.8 MPa, which is 100 MPa higher than the corresponding AA5182. The contributions of Orowan strengthening and grain boundary strengthening were obtained by calculation.
More Related Videos
14:51An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature
Published on: September 23, 2018
08:29Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)
Published on: January 7, 2019
Related Concept Videos
01:18Mechanical Characteristics of Steel
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
01:26Residual Stresses