Suppressing Defect Formation in Metal-Organic Framework Membranes via Plasma-Assisted Synthesis for Gas Separations

Metal-organic frameworks (MOFs) are considered as promising materials for membrane gas separations. Structural defects within a pure MOF membrane can considerably reduce its selectivity and possibly result in a nonselective separation. This work proposes a solution-phase synthesis with dielectric barrier discharge (DBD) plasma to suppress the formation of defects in the pure MOF membrane of CPO-8-BPY. Through comprehensive solid-state characterization with XRD, SEM, XPS, solid-state NMR, and XAFS, DBD plasma is demonstrated to facilitate deprotonation in the H₂aip linker, which leads to a smaller and more uniform particle size of CPO-8-BPY. The narrow grain size distribution effectively reduces the pinhole-type defects in the pure CPO-8-BPY membrane and endows it with good ideal selectivity for H₂/CH₄ (α_H = 28.2) and N₂/CH₄ (α_N = 5.4). The selectivity for H₂/CH₄ of this membrane from a mixed-gas permeation test is found to be 15.4. Molecular simulations are also performed to gain insights into the gas transport properties of this MOF. The results suggest that ligand rotation plays an important role in CPO-8-BPY when being applied to the membrane separation of N₂/CH₄.