D-spacing controllable GO membrane intercalated by sodium tetraborate pentahydrate for dye contamination wastewater...

Sodium tetraborate pentahydrate (STB) was intercalated into graphene oxide (GO) nanosheets to form a nanocomposite (STB@GO). Subsequently, it was self-assembled on a substrate membrane to prepare STB@GO nanofiltration membrane. The properties of the STB@GO powder samples and the nanofiltration membrane were studied using scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), contact angle (CA), and zeta potential. When the STB concentration was 1.0 g/L in the cross-linking reaction, the membrane was described as the STB₂@GO membrane and exhibited a large interlayer space (d-spacing = 1.347 nm), high hydrophilicity (CA = 22.2°), and high negative potential (zeta = -18.0 mV). Meanwhile, the pure water flux of the membrane was significantly increased by 56.60% than that of the GO membrane. In addition, the STB₂@GO membrane exhibited a favorable capability for dye rejection,98.52% for Evans blue (EB), 99.26% for Victoria blue B (VB), 91.94% for Alizarin yellow (AY), and 93.21% for Neutral red (NR). Furthermore, the STB₂@GO membrane performed better in dye separation under various types and concentrations of dye, pH values, and ions in solution. Thus, this study provides a promising method for preparing laminated GO nanofiltration membranes for dye wastewater treatment.