A Synergistic Flame Retardant System Based on Expandable Graphite, Aluminum (Diethyl-)Polyphospinate and Melamine...

Expandable graphite (EG), aluminum (diethyl)polyphosphinate (AlPi) and melamine polyphophate (MPP) was used as flame retardant multi-material additive in a polyamide 6 (PA6) matrix. Flame inhabitation performances were conducted by cone calorimeter, LOI and UL-94 tests, synergisms identified analyzed by TGA-FTIR and TGA-GC/MS and effects found were comprehensively discussed. SEM images were used for char residue characterization. For PA6 containing 20 wt.% EG and 5 wt.% AlPi/MPP (3:2), a well working synergism in limiting oxygen indices could be identified exhibiting the highest oxygen index (OI) measured: 46%. The study shows that the synergism due to the partial substitution of EG by AlPi/MPP can be attributed to two effects: (1) When PA6/AlPi/MPP mixtures decompose predominantly CO₂ evaporates in early decomposition stages. CO₂ evaporations was found to be sensitive to the heating rate applied, whereas specifically high heating rates increased the CO₂ yield measured. (2) Solid decomposition products of AlPi/MPP act as "glue" between expanded graphite and thus increase the mechanical residue stability.