Effect of Position and Structure of the Terminal Moieties in the Side Group on the Liquid Crystal Alignment Behavior...

We synthesized a series of polystyrene derivatives containing various side groups, such as the 4-(tert-butyl)-phenoxymethyl, 3-(tert-butyl)-phenoxymethyl, 2-(tert-butyl)-phenoxymethyl, 4-cumyl-phenoxymethyl, and 4-trityl-phenoxymethyl groups, through a polymer modification reaction to examine the liquid crystal (LC) alignment of these derivatives. In general, the vertical LC alignment on polymer films can be affected by the position and structure of the terminal moiety of the polymer side group. For example, the LC cells fabricated with 4-(tert-butyl)-phenoxymethyl-substituted polystyrene having a tert-butyl moiety as a para-type attachment to the phenoxy groups of the polystyrene derivatives exhibited vertical LC alignment, whereas the LC cells prepared from 3-(tert-butyl)- and 2-(tert-butyl)-phenoxymethyl-substituted polystyrene films exhibited planar LC alignment. In addition, the LC cells fabricated from 4-cumyl- and 4-trityl-phenoxymethyl-substituted polystyrene films with additional phenyl rings in the side groups exhibited planar LC alignment, in contrast to the LC alignment of the (tert-butyl)-phenoxymethyl-substituted polystyrene series. The vertical LC orientation was well correlated with the surface energy of these polymer films. For example, vertical LC orientation, which mainly originates due to the nonpolar tertiary carbon moiety having bulky groups, was observed when the surface energy of the polymer was lower than 36.6 mJ/m².