Boosting Unassisted Alkaline Solar Water Splitting Using Silicon Photocathode with TiO₂ Nanorods Decorated by...

To construct a highly efficient photoelectrochemical tandem device with silicon photocathode operating in alkaline conditions, it is desirable to develop stable and active catalysts which enable the photocathode to reliably perform under an alkaline environment. With nanostructured passivation layer and edge-exposed transition metal disulfides, silicon photocathode provides new opportunities for achieving unbiased alkaline solar water splitting. Here, the TiO₂ nanorod arrays decorated by edge-rich MoS₂ nanoplates are elaborately synthesized and deposited on p-Si. The vertically aligned TiO₂ nanorods fully stabilize the Si surface and improve anti-reflectance. Moreover, MoS₂ nanoplates with exposed edge sites provide catalytically active regions resulting in the kinetically favored hydrogen evolution under an alkaline environment. Interfacial energy band bending between p-Si and catalyst layers facilitates the transport of photogenerated electrons under steady-state illumination. Consequently, the MoS₂ nanoplates/TiO₂ nanorods/p-Si photocathode exhibits significantly improved photoelectrochemical-hydrogen evolution reaction (PEC-HER) performance in alkaline media with a high photocurrent density of 10 mA cm^-2 at 0 V versus RHE and high stability. By integrating rationally designed photocathode with earth-abundant Fe₆₀ (NiCo)₃₀ Cr₁₀ anode and perovskite/Si tandem photovoltaic cell, an unassisted alkaline solar water splitting is accomplished with a current density of 5.4 mA cm^-2 corresponding to 6.6% solar-to-hydrogen efficiency, which is the highest among p-Si photocathodes.