Indium sulfide deposited MIL-53(Fe) microrods: Efficient visible-light-driven photocatalytic reduction of hexavalent...

The ecosystems and human health were seriously threatened by hexavalent chromium (Cr(VI)) in wastewater. In this article, using the idea of the highly matched energy band structure between indium sulfide (In₂S₃) and MIL-53(Fe), a Type-II heterojunction has been constructed by loading In₂S₃ on MIL-53(Fe) microrod to overcome the fault like high recombination rates of photogenerated electron-holes of In₂S₃. The composite with 20:1 mass ratio of In₂S₃ to MIL-53(Fe) (IM-2) was adopted as an optimal sample for efficient photocatalytic Cr(VI) reduction under visible light. Various characterization techniques were used to verify the characteristics of composites and delved into the structure-effect relationship between this heterojunction and its activity. Results showed that the reaction rate constants of the photoreduction process over IM-2 was ~ 4 and 26 times higher than those of pure In₂S₃ and MIL-53(Fe), respectively, and the catalyst could maintain superior removal efficiency (88.6%) and steady crystal structure after four cycles. First-principles calculations further illustrated that the heterostructure formed between In₂S₃ and MIL-53(Fe) could effectively accelerate the separation of photogenerated electrons and holes, thus improving the photocatalytic reduction performance. Moreover, the active species analyses revealed that the superoxide radicals and electrons were mainly involved in the reduction of Cr(VI).