Comparison of Fracture Load of the Four Translucent Zirconia Crowns

Recently, translucent zirconia has become the most prevalent material used as a restorative material. This study aimed to compare the crown fracture load of the four most common different translucent zirconia brands available in the market at 1.5 mm thickness. Standardized tooth preparations for a full ceramic crown were designed digitally with software (AutoCAD) by placing a 1.0 mm chamfer margin and 1.5 mm occluso-cervical curvature for the crown sample manufacturing. Stylized crowns were chosen to control the thickness of the crown. The axial and occlusal thickness were standardized to 1.5 mm thickness except at the central pit, which was 1.3 mm thick. The STL file for the tooth dies was prepared using software (3Shape TRIOS^® Patient Monitoring, Copenhagen, Denmark). The tooth dies were printed with a resin material (NextDent Model 2.0, Vertex-Dental B.V., Soesterberg, The Netherlands) using a 3D printing software (3D Sprint^® Client Version 3.0.0.2494) from a 3D printer (NextDent™ 5100, Vertex-Dental B.V., Soesterberg, The Netherlands). The printing layer thickness was 50 µm. Then, a total of twenty-eight (N = 28) stylized crowns were milled out of AmannGirrbach (Amann Girrbach GmbH, Pforzheim, Germany) (n = 7), Cercon HT (Dentsply Sirona, Bensheim, Germany) (n = 7), Cercon XT (Dentsply Sirona, Bensheim, Germany) (n = 7), and Vita YZ XT (Zahnfabrik, Bäd Sackingen, Germany) (n = 7). Following sintering the crowns, sandblasting was performed and they were bonded to the tooth dies with the resin cement (RelyX U-200, 3M ESPE, Seefeld, Germany) and permitted to self-cure under finger pressure for 6 min. The crowns were loaded on the occlusal surface in a universal testing machine (MTS Centurion) with a stainless-steel ball indenter (7 mm radius) with a loading rate of 1 mm/min to contact the stylized crowns on each of the four cusps until failure. A rubber sheet (1.5 mm thickness) was positioned between the crown and indenter, which helped with the load distribution. Statistical analysis was done using SPSS version 20 (IBM Company, Chicago, USA). The fracture loads were analyzed using Dunnett's T3 test, and the number of cracks was analyzed using the Mann-Whitney U test among the groups. The significant level was set at p value = 0.05. The mean fracture loads were 3086.54 ± 441.74 N, 4804.94 ± 70.12 N, 3317.76 ± 199.80 N, and 2921.87 ± 349.67 N for AmannGirrbac, Cercon HT, Cercon XT, and Vita YZ XT, respectively. The mean fracture loads for the surfaces with the greatest number of cracks (excluding the occlusal surfaces) were on the lingual surface for AmannGirrbach and Cercon HT, on the distal and mesial for Cercon XT, and on the buccal for Vita YZ XT. We found that the AmannGirrbach had the most overall cracks. Cercon XT had the greatest number of occlusal cracks and appeared to be the most shattered. Cercon HT had the least number of cracks. In conclusion, Cercon HT presented the best strength properties, the highest fracture load, and no visible cracks. AmannGirrbach presented the lowest strength properties.