Performance of MoS₂/Zr Composite Coatings at Different Deposition Temperatures

The properties of the MoS₂/Zr coatings can be significantly affected by the deposition temperature. In this study, the MoS₂/Zr composite coatings were fabricated on the cemented carbide surface, utilizing the duplex deposition technology at various deposition temperatures. The effects of deposition temperature on the mechanical and friction properties of the MoS₂/Zr coatings were systematically studied. Results exhibited that as the deposition temperature increased, the adhesion force increased first and then decreased, and the coating thickness and micro-hardness gradually increased. Dry sliding tests against a hardened steel ring showed that the tribological behaviors and wear mechanisms of the MoS₂/Zr coatings varied with deposition temperature, which were due to the changing mechanical properties of coatings caused by the temperature. The coatings deposited at a temperature of 180 °C and 200 °C possessed preferable comprehensive mechanical and tribological properties.