DPD Study on the Interfacial Properties of PEO/PEO-PPO-PEO/PPO Ternary Blends: Effects of Pluronic Structure and...

Using the method of dissipative particle dynamics (DPD) simulations, we investigated the interfacial properties of PEO/PEO-PPO-PEO/PPO ternary blends composed of the Pluronics L64(EO₁₃PO₃₀EO₁₃), F68(EO₇₆PO₂₉EO₇₆), F88(EO₁₀₄PO₃₉EO₁₀₄), or F127(EO₁₀₆PO₇₀EO₁₀₆) triblock copolymers. Our simulations show that: (i) The interfacial tensions (γ) of the ternary blends obey the relationship γF68 < γL64 < γF88 < γF127, which indicates that triblock copolymer F68 is most effective in reducing the interfacial tension, compared to L64, F88, and F127; (ii) For the blends of PEO/L64/PPO and the F64 copolymer concentration ranging from c_cp = 0.2 to 0.4, the interface exhibits a saturation state, which results in the aggregation and micelle formation of F64 copolymers added to the blends, and a lowered efficiency of the L64 copolymers as a compatibilizer, thus, the interfacial tension decreases slightly; (iii) For the blends of PEO/F68/PPO, elevating the Pluronic copolymer concentration can promote Pluronic copolymer enrichment at the interfaces without forming the micelles, which reduces the interfacial tension significantly. The interfacial properties of the blends contained the PEO-PPO-PEO triblock copolymer compatibilizers are, thus, controlled by the triblock copolymer structure and the concentration. This work provides important insights into the use of the PEO-PPO-PEO triblock copolymer as compatibilizers in the PEO and PPO homopolymer blend systems.