Boron-Mediated Grain Boundary Engineering Enables Simultaneous Improvement of Thermoelectric and Mechanical...

Powder metallurgy introduces small structures of high-density grain boundaries into Bi₂ Te₃ -based alloys, which promises to enhance their mechanical and thermoelectric performance. However, due to the strong donor-like effect induced by the increased surface, Te vacancies form in the powder-metallurgy process. Hence, the as-sintered n-type Bi₂ Te₃ -based alloys show a lower figure of merit (ZT) value than their p-type counterparts and the commercial zone-melted (ZM) ingots. Here, boron is added to one-step-sintered n-type Bi₂ Te₃ -based alloys to inhibit grain growth and to suppress the donor-like effect, simultaneously improving the mechanical and thermoelectric (TE) performance. Due to the alleviated donor-like effect and the carrier mobility maintained in our n-type Bi₂ Te_2.7 Se_0.3 alloys upon the addition of boron, the maximum and average ZT values within 298-473 K can be enhanced to 1.03 and 0.91, respectively, which are even slightly higher than that of n-type ZM ingots. Moreover, the addition of boron greatly improves the mechanical strength such as Vickers hardness and compressive strength due to the synergetic effects of Hall-Petch grain-boundary strengthening and boron dispersion strengthening. This facile and cost-effective grain boundary engineering by adding boron facilitates the practical application of Bi₂ Te₃ -based alloys and can also be popularized in other thermoelectric materials.