Structural, Mechanical, and Decorative Properties of Sputtered TiN and Ti (N, C) Films for Orthodontic Applications;...

In this paper, we explore and modify the structural, mechanical, and decorative properties of films composed by TiN and Ti (N, C) with a wide range of N₂ gas flow during the deposition in order to be used on orthodontic systems. The films were grown using reactive DC magnetron sputtering from a pure Ti target and customized with C pellets onto Si and stainless steel 316L substrates. The structural properties were studied using X-ray diffraction and scanning electron microscopy, while the mechanical ones were obtained through hardness, elastic modulus, and friction coefficient. Moreover, the wear rate has been measured under an artificial saliva medium to simulate the oral cavity. The color of the films deposited onto stainless steel 316 L substrate was characterized through CIELab color code. Our findings show that the addition of N₂ and C in the Ti matrix improves the mechanical properties of the films. With the increase in the amount of N₂ and C, the hardness reaches a value of 739 HV, higher than the one reported in the literature (600 HV), a low value of the coefficient of elasticity (8.0 GPa), and also a low friction coefficient (0.30). Moreover, with the addition of N₂ and C in the Ti films, the color of the films changes from metallic aspect until "with" gold, which means that our coatings exhibit versatile mechanical and color characteristics to be used in orthodontic wires applications.