An Experimental Study on Mechanical Properties for the Static and Dynamic Compression of Concrete Eroded by Sulfate...

The mechanical properties of the static and dynamic compression of concrete eroded by a 15% sodium sulfate solution were explored with a 70-mm-diameter true triaxial static-dynamic comprehensive loading test system, and an analysis of the weakening mechanisms for the degree of macroscopic damage and microscopic surface changes of eroded concrete were conducted in combination with damage testing based on relevant acoustic characteristics and SEM scanning. The experience obtained in this paper is used to analyze and solve the problem that the bearing capacity of concrete buildings is weakened due to the decrease in durability under the special conditions of sulfate erosion. The results showed that, in a short time, the properties of concrete corroded by sulfate solution were improved to a certain extent due to continuous hydration. When the corrosion time was prolonged, the internal concrete structure was destroyed after it was eroded by sulfate, and its dynamic and static strength, deformability, and energy absorption were reduced to differing degrees, thus greatly inhibiting the overall mechanical performance of concrete; the dynamic compressive strength changed with strain that exhibited a significant strain rate effect; and, under the influence of sulfate erosion and hydration, the longitudinal wave velocity increased first and then decreased. The longitudinal wave velocity was slower than that of concrete under normal environment and distilled water immersion condition. SEM and acoustic wave analysis indicated that the internal concrete structure was destroyed after it was eroded by sulfate, and its dynamic and static strength, deformability, and energy absorption were reduced to differing degrees, thus greatly inhibiting the overall mechanical performance of concrete.