Exploring the photo-thermal conversion behavior and extinction coefficient of activated carbon nanofluids for direct...

This work aims to explore the optical and thermal conversion characteristics of activated carbon-solar glycol nanofluids with various volume fractions namely 0.2, 0.4, and 0.6%, respectively. Kigelia africana leaves were synthesized into porous activated carbon nanomaterials by using the high-temperature sintering process and the pyrolysis process in a muffle furnace. The experimental investigation was carried out with different nanofluid concentrations by using the solar simulator. Nanofluids were heated with the assistance of a solar simulator test system and the convection/conduction heat loss was decreased by using the glass as an insulating material around the test section. Prepared nanofluid with 0.6 vol% activated carbon augmented the thermal conductivity by 14.36% at 60°C. The maximum temperature difference of 10°C was attained at 0.6% volume concentrations of nanofluid as compared with base fluid (solar glycol). In addition, maximum receiver efficiency of 94.51% was attained at 0.6% volume fractions of activated carbon-based nanofluid compared with solar glycol thru a light radiation time of 600 s. Moreover, activated carbon-based nanofluid exhibited significantly higher absorption efficiency as the majority of the radiation was absorbed by the nanofluid. It is concluded that activated carbon-based nanofluids could be a suitable low-cost highly stable material for developing working fluid for direct absorbance solar collector-based applications.