SnS₂nanosheet arrays anchoring on functionalized carbon cloth for quasi-solid-state flexible supercapacitor with...

Increasing requirements for wearable devices stimulate the development of flexible energy storage components. Herein, a flexible integrated electrode consisting of SnS₂nanosheet arraysin situanchored on the functionalized carbon cloth was prepared via a facile one-step hydrothermal method. Through pretreatment of carbon cloth, rough morphology is appeared on the surface of carbon fiber, which is conducive to optimizing the accessible load of SnS₂. The SnS₂nanosheet arrays and the carbon fiber as conductive skeleton cooperate with each other to provide a highly open surface, leading to the enhancement in capacitance (194.4 mF cm^-2) and the outstanding retention after long-term service (86.5% after 10 000 cycles). A quasi-solid-state asymmetric flexible supercapacitor was assembled to evaluate the practical application under various conditions, suggesting satisfactory electrochemical performance as a maximum energy density of 10.95μWh cm^-2at the power density of 4.75 mW cm^-2and mechanical stability under actual conditions.