The Bond Strength of a Universal Adhesive System with Silane to Lithium Disilicates in Comparison with an Isolated
Danah Almaskin1, Zahra A Alzaher1, Masoumah Qaw2
1Fellowship Program in Prosthodontics, College of Dentistry, Imam Abdulrahman Bin Faisal University, Dammam, Saudi Arabia.
Purpose:
The aim of this in vitro study was to evaluate the effects of different durations of silane coupling agent application compared to a universal adhesive system regarding the shear bond strength of two ceramic materials.
Materials And Methods:
A total of 120 human molars were ground to the dentinal coronal third and then fixed into an acrylic resin holder. Lithium disilicate specimens were divided into two main groups according to the ceramic type: computer-aided design/computer-aided manufacturing IPS e.max CAD and heat-pressed Initial LiSi Press GC (dimensions of 4 × 3× 3 mm). Each main group was subdivided into 6 subgroups (n = 10) according to the duration of the silane and universal adhesive system application (20, 60, or 120 seconds) on the ceramic surface before cementation; then, the cementation procedures were performed. All specimens were subjected to 5000 thermal cycles at 5 and 55°C before testing. The shear bond strength was measured using a universal testing machine. ANOVA and Scheffe post hoc test multiple comparisons tests were conducted (α = 0.05).
Results:
The shear bond strength increased as the duration of the silane and universal adhesive system application increased. The highest bond value for each material was found for the silane application at 120 seconds, with a significant difference between 120 and 60, and 20 seconds for both e. max CAD and Initial LiSi materials (p = 0.029 and p ˂ 0.001, respectively). No significant difference was found between 60 and 20 seconds when silane and universal adhesive system were applied for both e. max CAD and Initial LiSi materials (p = 0.169 and p = 0.120, respectively). All groups treated with the silane primer showed significantly higher values than the universal adhesive system for each application time (p ˂ 0.001).
Conclusion:
Increasing the duration of the silane coupling agent and universal adhesive system application to 120 seconds on the ceramic surface before cementation improved the shear bond strength of the ceramic-cement interface. Ceramic pretreatment with silane could be an essential step for bonding ceramic to dentin regardless of silane presence in the universal adhesive system.
Related Concept Videos
01:12Bonding and Strength of Aggregate
02:40Chemical Bonds
Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons...