Fretting Fatigue Performance of Unidirectional, Laminated Carbon Fibre Reinforced Polymer Straps at Elevated Service

Danijela Stankovic1,2, Luke A Bisby1, Zafiris Triantafyllidis2

  • 1Institute for Infrastructure & Environment, School of Engineering, University of Edinburgh, Mayfield Road, Edinburgh EH9 3JL, UK.

Polymers
|October 13, 2021
PubMed

Keywords:
S–N curvecarbon fibre-reinforced polymer (CFRP) strapsfatigue performancepin-loadedservice temperatureunidirectional (UD) composite straps

More Related Videos

A Testing Platform for Durability Studies of Polymers and Fiber-reinforced Polymer Composites under Concurrent Hygrothermo-mechanical Stimuli07:15

A Testing Platform for Durability Studies of Polymers and Fiber-reinforced Polymer Composites under Concurrent Hygrothermo-mechanical Stimuli

Published on: December 11, 2014

14.0K
Artificial Thermal Ageing of Polyester Reinforced and Polyvinyl Chloride Coated Technical Fabric07:48

Artificial Thermal Ageing of Polyester Reinforced and Polyvinyl Chloride Coated Technical Fabric

Published on: January 29, 2020

6.7K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
287
Stress-Strain Diagram - Ductile Materials01:24

Stress-Strain Diagram - Ductile Materials

The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...
1.1K
Stresses under Combined Loadings01:23

Stresses under Combined Loadings

When analyzing a bent tube with a circular cross-section subjected to multiple forces, it is crucial to determine the stress distribution in order to maintain structural integrity under varied load conditions.
The process begins by slicing the tube at critical points and analyzing the internal forces and stress components at these sections, focusing on the centroid. Normal stresses, generated by axial forces and bending moments, are either compressive or tensile and vary across the section from...
256
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
328
Thermal Strain01:19

Thermal Strain

Thermal strain is a concept that arises when we consider how temperature changes affect structures. Unlike the conventional assumption that structures remain constant under load, real-world scenarios often involve temperature fluctuations that can significantly impact these structures. Consider a homogeneous rod with a uniform cross-section resting freely on a flat horizontal surface. If the rod's temperature increases, the rod elongates. This elongation is proportional to the temperature...
2.6K
Temperature Dependent Deformation01:12

Temperature Dependent Deformation

In a nonhomogeneous rod made up of steel and brass, restrained at both ends and subjected to a temperature change, several steps are involved in calculating the stress and compressive load. Due to the problem's static indeterminacy, one end support is disconnected, allowing the rod to experience the temperature change freely. Next, an unknown force is applied at the free end, triggering deformations in the rod's steel and brass portions. These deformations are then calculated and added...
225