Bivalves rapidly repair shells damaged by fatigue and bolster strength

Hard external armors have to defend against a lifetime of threats yet are traditionally understood by their ability to withstand a single attack. Survival of bivalve mollusks thus can depend on the ability to repair shell damage between encounters. We studied the capacity for repair in the intertidal mussel Mytilus californianus by compressing live mussels for 15 cycles at ∼79% of their predicted strength (critically fracturing 46% of shells), then allowing the survivors 0, 1, 2 or 4 weeks to repair. Immediately after fatigue loading, mussel shells were 20% weaker than control shells that had not experienced repetitive loading. However, mussels restored full shell strength within 1 week, and after 4 weeks shells that had experienced greater fatiguing forces were stronger than those repetitively loaded at lower forces. Microscopy supported the hypothesis that crack propagation is a mechanism of fatigue-caused weakening. However, the mechanism of repair was only partially explained, as epifluorescence microscopy of calcein staining for shell deposition showed that only half of the mussels that experienced repetitive loading had initiated direct repair via shell growth around fractures. Our findings document repair weeks to months faster than demonstrated in other mollusks. This rapid repair may be important for the mussels' success contending with predatory and environmental threats in the harsh environment of wave-swept rocky coasts, allowing them to address non-critical but weakening damage and to initiate plastic changes to shell strength. We highlight the significant insight gained by studying biological armors not as static structures but, instead, as dynamic systems that accumulate, repair and respond to damage.