Ultrastretchable, Adhesive, and Antibacterial Hydrogel with Robust Spinnability for Manufacturing Strong Hydrogel...

The ultrastretchable (over 12 400%) hydrogel with long-lasting adhesion, strong antibacterial activity, and robust spinnability is developed based on the oxidative decarboxylation and quinone-catechol reversible redox reaction induced by Ag-lignin nanoparticles in a precursor solution containing citric acid (CA), acrylic acid (AA), and poly (acrylamide-co-acrylic acid) (P(AAm-co-AA)). With massive reversible interactions including hydrogen bonds and electrostatic forces, such hydrogel exhibits promising injectability and is facilely spun via manual drawing, draw-spinning, and electrospinning for manufacturing strong hydrogel micro/nanofibers. The resulting fibers exhibit excellent mechanical properties, including tensile stress of 422.0 MPa, strain of 86.5%, Young's modulus of 8.7 GPa, and toughness of 281.6 MJ m^-3 . The hydrogel microfibers obtained from a house-built spinner are scaled-up fabricated while retaining promising mechanical properties, as evidenced by lifting a load (317.2 g) using the spun fibers of ≈33 000 times lighter weight (9.5 mg), indicating their great potentials in the applications such as net and safety cord which require robust mechanical properties. Moreover, assisted by a commercial electrospinning machine, nanosized hydrogel fibers are facilely spun on personal protective equipment such as a mask to offer an antiseptic coating with near 100% killing efficiency against airborne bacteria aerosols, demonstrating the capability of spun hydrogel fibers on disinfection-related applications.