Synthesis, Characteristics, Oil Adsorption, and Thermal Insulation Performance of Cellulosic Aerogel Derived from...

Cellulosic aerogel from water hyacinth (WH) was synthesized to address the dual environmental issues of water hyacinth pollution and the production of a green material. Raw WH was treated with sodium hydroxide (NaOH) with microwave assistance and in combination with hydrogen peroxide (H₂O₂). The results from X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, and scanning electron microscopy (SEM) showed that lignin and hemicellulose were markedly decreased after treatment, reducing from 24.02% hemicellulose and 5.67% lignin in raw WH to 8.32 and 1.92%, respectively. Cellulose aerogel from the pretreated WH had a high porosity of 98.8% with a density of 0.0162 g·cm^-3 and a low thermal conductivity of 0.030 W·m^-1·K^-1. After modification with methyl trimethoxysilane (MTMS) to produce a highly hydrophobic material, WH aerogel exhibited high stability for oil absorption at a capacity of 43.3, 43.15, 40.40, and 41.88 (g·g^-1) with diesel oil (DO), motor oil (MO), and their mixture with water (DO + W and MO + W), respectively. The adsorption remained stable after 10 cycles.