Properties of pullulan-based blend films as affected by alginate content and relative humidity

Pullulan-sodium alginate blend films were prepared and characterized as a function of water activity (a_w). At low a_w, the incorporation of alginate into pullulan film increased the tensile strength and elastic modulus, but decreased the elongation at break of the composite films; the opposite trends were observed at elevated a_w. Above 0.43 a_w, water exerted a typical plasticization effect upon the biopolymer blends. As a_w increased from 0.23 to 0.43, an anti-plasticization effect was observed as tensile strength and elastic modulus increased. The glass transition temperature of all samples decreased substantially as aw increased from 0.23 to 0.84 due to the plasticization effect of water. Within this a_w range, one transition temperature was observed for all film specimens. The stretching vibration band of O-H was investigated using attenuated total reflection Fourier transform infrared spectroscopy to identify the various species of water interacting with the polysaccharide films.