Silver carboxylate-doped titanium dioxide-polydimethylsiloxane coating decreases Cutibacterium acnes adherence and
Dioscaris R Garcia1, Ellis M Berns2, Carole S L Spake2
1The Warren Alpert Medical School of Brown University, Providence, RI, USA; Department of Orthopaedic Surgery, Warren Alpert Medical School of Brown University, Providence, RI, USA; Weiss Center for Orthopaedic Trauma Research, Rhode Island Hospital, Providence, RI, USA.
Background Context:
Cutibacterium acnes (C. acnes) is a gram-positive facultative anaerobe found in the deep sebaceous follicles of the skin on the shoulder and back. C. acnes has been increasingly recognized as a pathogen in spinal surgical site infection (SSI) especially in the presence of instrumentation.
Purpose:
This study assesses whether a silver carboxylate-doped titanium dioxide-polydimethylsiloxane (TiO2-PDMS) coating can decrease C. acnes adherence and biofilm formation on PEEK and four other commonly used spinal implant materials, stainless steel, cobalt chromium, titanium, and titanium alloy.
Study Design:
We compared the adherence of C. acnes over 24 hours between uncoated, 95:5 TiO2 to PDMS ratio with 10× silver carboxylate coating and a 100% silver carboxylate coating on each implant material, which were uniformly saw cut and sterilized. Implants were then subjected to scanning electron microscopy (SEM) and confocal scanning laser microscopy (CSLM).
Methods:
Samples were coated using 95:5 TiO2-PDMS 10× silver carboxylate, 100% silver carboxylate, or left uncoated. C. acnes was applied onto the samples and allowed to adhere for periods of 4, 8, 12, 16, or 20 hours. Nonadherent bacteria were then washed from the samples. These samples were then allowed to continue incubating for a total of 24 hours. SEM and confocal laser scanning microscope were used to visualize all samples for the presence of biofilm and quantification of C. acnes adherence at each time point.
Results:
The 95:5 TiO2-PDMS 10× silver carboxylate coating was able to significantly decrease C. acnes adherence on PEEK after 8, 12, 16, and 20 hours of adherence. No statistical difference was found between the 95:5 TiO2-PDMS 10× silver carboxylate coating and the 100% silver carboxylate positive control. We previously observed extensive C. acnes biofilm formation on uncoated PEEK, but none on PEEK coated with either the 95:5 TiO2-PDMS 10× silver carboxylate or 100% Ag coating . Furthermore, no biofilm formation was observed on stainless steel, cobalt chromium, titanium, and titanium alloy coated with 95:5 TiO2-PDMS 10× silver carboxylate or 100% Ag coating.
Conclusion:
A 95:5 TiO2-PDMS 10× silver carboxylate coating decreases C. acnes adhesion and prevents biofilm formation on PEEK and other common orthopedic implant materials.
Clinical Significance:
A 95:5 TiO2-PDMS 10× silver carboxylate coating may help decrease spinal SSI due to C. acnes, especially in procedures with instrumentation.
More Related Videos
10:17Methodologies for Studying B. subtilis Biofilms as a Model for Characterizing Small Molecule Biofilm Inhibitors
Published on: October 9, 2016
08:20Systematic Approach to Identify Novel Antimicrobial and Antibiofilm Molecules from Plants' Extracts and Fractions to Prevent Dental Caries
Published on: March 31, 2021