Synthesis and Tribological Characterization of Ti₃SiC₂/ZnO Composites

Dense Ti₃SiC₂/ZnO composites were sintered at different temperatures by spark plasma sintering (SPS). The effects of sintering temperature on composition and mechanical properties of Ti₃SiC₂/ZnO composites were studied. The tribological behaviors of Ti₃SiC₂/ZnO composites/Inconel 718 alloy tribo-pairs at elevated temperature from 25 °C to 800 °C were discussed. The experimental results showed that the initial decomposition temperature of the Ti₃SiC₂/ZnO composite was 1150 °C, and Ti₃SiC₂ decomposed into TiC. When the decomposition temperature was higher than 1150 °C, the compositions of the Ti₃SiC₂/ZnO composites were Ti₃SiC₂, ZnO, and TiC. It was found that Ti₃SiC₂/ZnO composites had better self-lubricating performance than Ti₃SiC₂ at elevated temperature from 600 °C to 800 °C, which was owing to material transfers of tribo-pairs and sheared oxides generated by tribo-oxidation reactions.