2 μm passively mode-locked thulium-doped fiber lasers with Ta₂AlC-deposited tapered and side-polished fibers

In this work, mode-locked thulium-doped fiber lasers operating in the 2 µm wavelength region were demonstrated using tantalum aluminum carbide (Ta₂AlC)-based saturable absorbers (SAs) utilizing the evanescent wave interaction. The Ta₂AlC MAX Phase was prepared by dissolving the Ta₂AlC powder in isopropyl alcohol and then deposited onto three different evanescent field-based devices, which were the tapered fiber, side-polished fiber, and arc-shaped fiber. Flame-brushing and wheel-polishing techniques were used to fabricate the tapered and arc-shaped fibers, respectively, while the side-polished fiber was purchased commercially. All three SA devices generated stable mode-locked pulses at center wavelengths of 1937, 1931, and 1929 nm for the tapered, side-polished, and arc-shaped fibers. The frequency of the mode-locked pulses was 10.73 MHz for the tapered fiber, 9.58 MHz for the side-polished fiber, and 10.16 MHz for the arc-shaped fiber. The measured pulse widths were 1.678, 1.734, and 1.817 ps for each of the three SA devices. The long-term stability of the mode-locked lasers was tested for each configuration over a 2-h duration. The lasers also showed little to no fluctuations in the center wavelengths and the peak optical intensities, demonstrating a reliable, ultrafast laser system.