Spray drying induced engineering a hierarchical reduced graphene oxide supported heterogeneous Tin dioxide and Zinc...

In this work, a hierarchical reduced graphene oxide (RGO) supportive matrix consisting of both larger two-dimensional RGO sheets and smaller three-dimensional RGO spheres was engineered with ZnO and SnO₂ nanoparticles immobilized. The ZnO and SnO₂ nanocrystals with controlled size were in sequence engineered on the surface of the RGO sheets during the deoxygenation of graphene oxide sample (GO), where the zinc-containing ZIF-8 sample and metal tin foil were used as precursors for ZnO and SnO₂, respectively. After a spray drying treatment and calcination, the final ZnO@SnO₂/RGO-H sample was obtained, which delivered an outstanding specific capacity of 982 mAh·g^-1 under a high current density of 1000 mA·g^-1 after 450 cycles. Benefitting from the unique hierarchical structure, the mechanical strength, ionic and electric conductivities of the ZnO@SnO₂/RGO-H sample have been simultaneously promoted. The joint contributions from pseudocapacitive and battery behaviors in lithium-ion storage processes bring in both large specific capacity and good rate capability. The industrially mature spray drying method for synthesizing RGO based hierarchical products can be further developed for wider applications.