The Influence of Undercooling ΔT on the Structure and Tensile Strength of Grey Cast Iron

Inoculation of cast iron has become a commonly used metallurgical process, which is carried out in a foundry in order to improve the mechanical properties of utility alloys. It consists in changing the physicochemical state of the melted alloy. This change is caused by the introduction of cast iron with a low ability to nucleate graphite, shortly before pouring a small mass of the substance-an inoculant that increases the number of active nuclei. It is also justified that the literature often connects an increase in the tensile strength UTS of the inoculated grey cast iron, with changes in the characteristics of the particles of graphite. However, in strongly hypoeutectic cast iron, in which a large number of primary austenite grains crystallize, the interdendritic distribution of graphite is usually the result. It also follows that the nature of the graphite precipitates is determined by the mutual relations between the interfacial distances in eutectic grains and the interdendritic distances in the grains of primary austenite occurring in the Fe-C alloys. The article presents the influence of the inoculant on the characteristics of the precipitation of primary austenite grains in relation to the sulphur content in grey cast iron with flake graphite. The study also showed that primary grains in grey cast iron have a great influence on mechanical properties, such as the tensile strength UTS. In this case, the key is to know the value of the degree of undercooling ΔT. The type of inoculant used affects the ΔT value. The study related the number of N primary austenite grains with the degree of undercooling ΔT and the tensile strength UTS with the number of primary austenite N grains.