Impact of Immediate Dentin Sealing Using Universal Adhesive under Simulated Pulp Pressure on Microtensile Bond
Emad Abd Elfatah Abo-Alazm1, Rehab Khalil Safy2
1Department of Restorative Dentistry, Egyptian Russian University, Badr City, Cairo Governorate, Egypt.
Objective:
The aim of this study was to investigate the effect of immediate dentin sealing (IDS) technique using universal adhesive under simulated pulp pressure on microtensile bond strength (μTBS) of indirect resin composite restorations and dentin permeability.
Materials And Methods:
Fifty extracted caries-free human third molars were used for specimens' preparation. Each molar's occlusal table was abraded flat and their roots were separated under continuous water cooling. Forty specimens were used for microtensile bond strength test (μTBST) evaluation. The μTBST specimens were randomly assigned to two groups according to the dentin sealing time; Immediate dentin sealing (IDS) and delayed dentin sealing (DDS). Each group was further subdivided into two subgroups according to the adhesive system used for dentin sealing: iBOND self-etch adhesive and GLUMA Bond Universal. All specimens were exposed to simulated pulp pressure for 1 week then restored using computer-aided design/computer-aided manufacturing (CAD/CAM) resin composite blocks. The μTBS was evaluated for all tested subgroups after 24 hours and 6 months of water storage. The remaining 10 teeth were used for the preparation of dentin discs for dentin permeability evaluation. They were divided into two groups according to type of self-etch adhesive used. Fluid filtration rate was evaluated after etching, with smear layer and after adhesive application. Results obtained were statistically analyzed using Shapiro-Wilk test and Weibull analysis.
Results:
Statistically significant difference was recorded between µTBS mean values of both IDS and DDS techniques at 24 hours and after 6 months of water storage. GLUMA Bond Universal adhesive had significantly higher bond strength compared with iBond at both IDS and DDS techniques, but both adhesives showed a significant reduction in the Weibull characteristic strength after 6 months of water storage. Significant reduction in dentin permeability was recorded by both adhesives without any significant difference between them.
Conclusions:
The IDS technique using universal adhesive in self-etch mode is an effective strategy for improving the final bond strength of CAD/CAM resin composite restorations and reducing dentin permeability.