The Effect of Translucency and Surface Treatment on the Flexural Strength of Aged Monolithic Zirconia

Rashin Giti1, Benika Abbasi1

  • 1Department of Prosthodontics, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.

International Journal of Dentistry
|November 19, 2021
PubMed
Abstract

More Related Videos

Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins03:02

Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins

Published on: January 17, 2025

564
Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)08:29

Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)

Published on: January 7, 2019

11.5K

Related Concept Videos

Flexural Stress01:16

Flexural Stress

When analyzing bending in symmetric members, it's crucial to understand how stresses distribute when subjected to bending moments. This stress distribution is effectively described by applying fundamental mechanics and material science principles, particularly Hooke's Law for elastic materials.
Hooke's Law states that within the material's elastic limits, stress is directly proportional to strain. In a member experiencing a bending moment, the strain at any point is relative to...
423
Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
267
Toughness and Hardness of Aggregate01:22

Toughness and Hardness of Aggregate

Toughness and hardness are critical properties of aggregate materials used in concrete, particularly on pavement surfaces and industrial flooring subjected to heavy loads. Toughness is defined as the aggregate's resistance to failure by impact and is measured by the aggregate impact value (AIV). For this, the aggregate impact value test is performed, wherein the impact is delivered by a standard hammer, which falls freely under its own weight onto the aggregates. The aggregates fragment in...
372
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
245
Tensile Strength Considerations of Concrete01:16

Tensile Strength Considerations of Concrete

Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
The dimensions and shape of a concrete specimen...
236
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
324