Comparison between Hydrofluoric Acid and Single-Component Primer as Conditioners on Resin Cement Adhesion to Lithium...

This study aimed at evaluating the effects of different surface conditionings on the microshear bond strength (µSBS) of a self-adhesive resin cement to VITA Suprinity (ZLS) and IPS e.max CAD (LD). Three surface conditioning protocols were performed on ZLS and LD before luting with a self-adhesive resin cement (RelyX Unicem 2, RXU): hydrofluoric acid (HF), HF + silane (HF + S), or Monobond Etch & Prime (EP). In each group, 15 cylindrical buildups of RXU were prepared on five milled bars and submitted to a µSBS test. Data were statistically analyzed with two-way ANOVA and Tukey's post hoc test (p < 0.05). Failure modes were recorded and classified as adhesive, mixed, cohesive in resin, or ceramic, and statistically analyzed with Fisher's exact test (p = 0.05). One additional bar per group was used for the morphological characterization of the conditioned surface by means of SEM. The material per se did not significantly influence adhesion (p = 0.744). Conditioning protocol was a significant factor: EP yielded significantly higher μSBS than HF (p = 0.005), while no significant differences emerged between EP and HF + S (p = 0.107), or HF + S and HF (p = 0.387). The material-conditioning protocol interaction was not statistically significant (p = 0.109). Significant intergroup differences were found in distribution of failure modes: mixed failures were predominant in the ZLS/EP group, while the other groups showed a prevalence of adhesive failures. The self-etching primer showed promising results in terms of immediate bond strength of a self-adhesive resin cement to lithium-silica-based glass ceramics, suggesting its alternative use to hydrofluoric acid and silane conditioning protocols.