Superwicking Functionality of Femtosecond Laser Textured Aluminum at High Temperatures

An advanced superwicking aluminum material based on a microgroove surface structure textured with both laser-induced periodic surface structures and fine microholes was produced by direct femtosecond laser nano/microstructuring technology. The created material demonstrates excellent wicking performance in a temperature range of 23 to 120 °C. The experiments on wicking dynamics show a record-high velocity of water spreading that achieves about 450 mm/s at 23 °C and 320 mm/s at 120 °C when the spreading water undergoes intensive boiling. The lifetime of classic Washburn capillary flow dynamics shortens as the temperature increases up to 80 °C. The effects of evaporation and boiling on water spreading become significant above 80 °C, resulting in vanishing of Washburn's dynamics. Both the inertial and visco-inertial flow regimes are insignificantly affected by evaporation at temperatures below the boiling point of water. The boiling effect on the inertial regime is small at 120 °C; however, its effect on the visco-inertial regime is essential. The created material with effective wicking performance under water boiling conditions can find applications in Maisotsenko cycle (M-cycle) high-temperature heat/mass exchangers for enhancing power generation efficiency that is an important factor in reducing CO₂ emissions and mitigation of the global climate change.