Lithium and Potassium Cations Affect the Performance of Maleamate-Based Organic Anode Materials for Potassium- and Lithium-Ion Batteries

In this study we prepared potassium-ion batteries (KIBs) displaying high output voltage and, in turn, a high energy density, as replacements for lithium-ion batteries (LIBs). Organic electrode materials featuring void spaces and flexible structures can facilitate the mobility of K⁺ to enhance the performance of KIBs. We synthesized potassium maleamate (K-MA) from maleamic acid (MA) and applied as an anode material for KIBs and LIBs, with 1 M potassium bis(fluorosulfonyl)imide (KFSI) and 1 M lithium bis(fluorosulfonyl)imide (LiFSI) in a mixture of ethylene carbonate and ethyl methyl carbonate (1:2, v/v) as respective electrolytes. The K-MA_KFSI anode underwent charging/discharging with carbonyl groups at low voltage, due to the K···O bond interaction weaker than Li···O. The K-MA_KFSI and K-MA_LiFSI anode materials delivered a capacity of 172 and 485 mA h g^-1 after 200 cycles at 0.1C rate, respectively. K-MA was capable of accepting one K⁺ in KIB, whereas it could accept two Li⁺ in a LIB. The superior recoveries performance of K-MA_LiFSI, K-MA_KFSI, and Super P_KFSI at rate of 0.1C were 320, 201, and 105 mA h g^-1, respectively. This implies the larger size of K⁺ can reversibly cycling at high rate.