Oxygen-vacancy abundant alpha bismuth oxide with enhanced cycle stability for high-energy hybrid supercapacitor...

Bi₂O₃ is an outstanding electrode material due to its high theoretical specific capacity. Hence, the synthesis of δ-Bi₂O₃ materials with high oxygen-vacancy contents could improve their electrochemical performances but causes easy conversion to α-Bi₂O₃ with low oxygen-vacancy contents, leading to poor cycling stability and limited practical applications. To overcome these problems, an effective strategy for constructing high oxygen vacancies α-Bi₂O₃ on activated carbon fiber paper (ACFP) is developed in this study. To this end, ACFP/Bi(OH)₃ is first synthesized by the solvothermal method and then converted to ACFP/α-Bi₂O₃ by in situ electrochemical activation. The proposed innovative electrochemical method quickly and easily introduces oxygen vacancies while preserving the three-dimensional structure, thereby promoting the charge transfer and ions diffusion in ACFP/α-Bi₂O₃. Consequently, the specific capacity of ACFP/α-Bi₂O₃ reaches 906C g^-1 at 1 A g^-1, and the capacity retention remains above 70% after 3000 cycles, a value higher than that of δ-Bi₂O₃ (45%). Furthermore, the hybrid supercapacitor device assembled by ACFP/α-Bi₂O₃ delivers a maximum energy density of 114.9 Wh kg^-1 at 900 W kg^-1 and outstanding cycle stability with 73.56 % retention after 5500 cycles. In sum, the proposed ACFP/α-Bi₂O₃ with high performance and good stability looks promising for use as bismuth-based anode materials in supercapacitors and aqueous batteries.