Efficacious CO₂ Adsorption and Activation on Ag Nanoparticles/CuO Mesoporous Nanosheets Heterostructure for CO₂...

It is an ongoing pursuit for researchers to precisely control the catalyst's surface for high-performance CO₂ electrochemical reduction (CO₂ER). In this work, CuO mesoporous nanosheets (CuO MNSs) with rough edges decorated by small Ag nanoparticles (Ag NPs) with a tunable amount of Ag were synthesized on a Cu foil at normal atmospheric temperature through two-step solution-phase reactions for CO₂ER to CO. In this special Ag NPs/CuO MNSs heterostructure, the mesoporous CuO NSs with rough edges favored gas infiltration, while decorated Ag NPs expanded the active sites for CO₂ molecule adsorption. Ag NPs endowed Ag NPs/CuO MNSs with good electrical conductivity and promoted the adsorbed CO₂ molecules to obtain electrons from the catalyst. Especially, the Ag-CuO interface stabilized the *COOH intermediate with strong bonding, which is important in boosting CO₂ER to CO. The optimal Ag_1.01%/CuO can catalyze CO₂ER to CO with a Faradaic efficiency of 91.2% and a partial current density of 10.5 mA cm^-2 at -0.7 V. Moreover, it exhibited prominent catalytic stability, retaining 97.8% of the initial current density and 97.6% of the original Faradaic efficiency for CO after 12 h of testing at -0.7 V. Notably, the Faradaic efficiency of CO on Ag_1.01%/CuO can retain over 80% in the potential area from -0.6 to -0.9 V, embodying its high selectivity for CO. This work develops precious metal/metal oxide heterostructures with a low precious metal loading for efficacious CO₂ER to CO and beyond.