Microstructural Evaluation of Phase Instability in Large Bandgap Metal Halide Perovskites

The optoelectronic performance of organic-inorganic halide perovskite (OIHP)-based devices has been improved in recent years. Particularly, solar cells fabricated using mixed-cations and mixed-halides have outperformed their single-cation and single-halide counterparts. Yet, a systematic evaluation of the microstructural behavior of mixed perovskites is missing despite their known composition-dependent photoinstability. Here, we explore microstructural inhomogeneity in (FAPbI₃)(MAPbBr₃)_1- using advanced scanning probe microscopy techniques. Contact potential difference (CPD) maps measured by Kelvin probe force microscopy show an increased fraction of grains exhibiting a low CPD with flat topography as MAPbBr₃ concentration is increased. The higher portion of low CPD contributes to asymmetric CPD distribution curves. Chemical analysis reveals these grains being rich in MA, Pb, and I. The composition-dependent phase segregation upon illumination, reflected on the emergence of a low-energy peak emission in the original photoluminescence spectra, arises from the formation of such grains with flat topology. Bias-dependent piezo-response force microscopy measurements, in these grains, further confirm vigorous ion migration and cause a hysteretic piezo-response. Our results, therefore, provide insights into the microstructural evaluation of phase segregation and ion migration in OIHPs pointing toward process optimization as a mean to further enhance their optoelectronic performance.