Cyclic fatigue tests on non-anatomic specimens of dental ceramic materials: A scoping review

The aim of the present scoping review was to identify and discuss the methods, testing parameters, and characteristics used to induce cyclic fatigue on non-anatomic dental ceramic specimens. In vitro studies written in English which evaluated commercially-available non-anatomic dental ceramic specimens subjected to mechanical cyclic fatigue were selected. The search was performed in the PubMed, Scopus and Web of Science databases. The initial search yielded 1,636 articles, of which 81 were included. Based on the collected data, most of the included studies evaluated dental ceramic specimens cemented to supporting substrate (n= 42; 51.9%); used step-stress (n= 35; 42.2%) accelerated fatigue test, loading frequencies above 10 Hz (n= 31, 35.6%), stainless steel (n = 28, 32.6%) load applicator with spherical shaped tip 40 mm diameter (n= 25, 30.9%); applied only axial loads (n= 77, 95.1%); and considered a wet testing environment (n= 65, 78.3%). The definition of test geometry, method, and testing parameters must be cautiously considered according to the study objective and the scenario that is simulated. Accelerated fatigue tests, load frequencies up to 20 Hz, a 40 mm stainless steel spherical load applicator and a wet testing environment are the major common defined parameters presented in the existing literature. More studies exploring the influence of such factors on fatigue mechanism are necessary.