Reasons for Reduced Moisture Resistance of Sulfur-Extended Asphalt Concrete

Huu Tuan Le1, Evgenij V Korolev1, Anna N Grishina1

  • 1REC "Nanomaterials and Nanotechnology", Research Center "MGSU Stroy-Test", National Research Moscow State University of Civil Engineering, 129337 Moscow, Russia.

Materials (Basel, Switzerland)
|December 10, 2021
PubMed

Keywords:
and magnesium saltschemical interaction of sulfur with mineral fillershydrogen sulfidemoisture resistancesulfur dioxidesulfur-bitumen bindersulfur-bitumen pastesulfur-containing water-soluble calciumsulfur-extended asphalt concretetechnical sulfur

More Related Videos

Synthesis of Terpolymers at Mild Temperatures Using Dynamic Sulfur Bonds in PolyS-Divinylbenzene09:16

Synthesis of Terpolymers at Mild Temperatures Using Dynamic Sulfur Bonds in PolyS-Divinylbenzene

Published on: May 20, 2019

7.8K
Measurement of the Rheology of Crude Oil in Equilibrium with CO2 at Reservoir Conditions10:38

Measurement of the Rheology of Crude Oil in Equilibrium with CO2 at Reservoir Conditions

Published on: June 6, 2017

12.9K

Related Concept Videos

Sulfate Attack on Concrete01:29

Sulfate Attack on Concrete

Sulfate attack on concrete is a deterioration process characterized by a whitish discoloration beginning at the edges and corners, accompanied by cracking and spalling. This phenomenon occurs when sulfates react with the components of hardened concrete, forming compounds like calcium sulfate and calcium sulfoaluminate which occupy more space than the substances they replace, causing the concrete to expand and disrupt.
Sulfates from sources like soil, groundwater, or industrial effluents...
335
Design Example: Managing Concrete Workability01:14

Design Example: Managing Concrete Workability

This example deals with managing the workability of concrete for a raft foundation project under hot weather conditions. Workability is crucial for ensuring the concrete is easy to place, compact, and finish. In this scenario, a slump test — a common method to measure the workability of fresh concrete — initially indicated low workability. This was attributed to the rapid water loss from the concrete mix, exacerbated by the high temperatures causing the course aggregates to heat up.
135
Frost Resistant Concrete01:29

Frost Resistant Concrete

Concrete's susceptibility to frost damage during freeze-thaw cycles demands strategic measures to enhance its frost resistance. Employing techniques like air entrainment, adjusting the water-cement ratio, proper curing, and selecting appropriate aggregates are essential.
Introducing microscopic air bubbles into the concrete mix through air entrainment creates small voids that accommodate ice expansion, thereby reducing internal pressures and preventing cracking. The optimal amount of...
154
Hot Weather Concreting01:20

Hot Weather Concreting

Concreting at elevated temperatures accelerates the hydration process, leading to quicker setting but potentially reducing the long-term strength of the concrete structure. Additionally, low air humidity fosters rapid moisture loss from the concrete, resulting in reduced workability, pronounced plastic shrinkage, and a higher likelihood of crazing.
Mitigating the heat increase in concrete can be economically achieved by shading aggregate stockpiles to prevent heating from solar radiation,...
132
Types of Cement I01:21

Types of Cement I

Portland cement comes in several types, each with distinct properties and applications based on their chemical composition and hydration characteristics:
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
199
Drying Shrinkage01:21

Drying Shrinkage

When hardened concrete is exposed to air with a relative humidity of less than 100 percent, it begins to lose the free water within its capillaries. As this water evaporates, the water initially adsorbed onto the calcium silicate hydrates migrates towards these now empty spaces and eventually evaporates as well. Over time, as more water leaves, the volume of the concrete decreases, a phenomenon known as drying shrinkage.
A portion of this drying shrinkage can be reversed; if the concrete is...
179