Core-Shell Fe₂O₃@La_1-xSr_xFeO_3-δ Material for Catalytic Oxidations: Coverage of Iron Oxide Core, Oxygen Storage...

A series of Fe₂O₃@LSF (La_0.8Sr_0.2FeO_3-δ perovskite) core-shell materials (CSM) was prepared by infiltration of LSF precursors gel containing various complexants and their mixtures to nanocrystalline aggregates of hematite followed by thermal treatment. The content of LSF phase and amount of carboxyl groups in complexant determine the percent coverage of iron oxide core with the LSF shell. The most conformal coating core-shell material was prepared with citric acid as the complexant, contained 60 wt% LSF with 98% core coverage. The morphology of the CSM was studied by HRTEM-EELS combined with SEM-FIB for particles cross-sections. The reactivity of surface oxygen species and their amounts were determined by H₂-TPR, TGA-DTG, the oxidation state of surface oxygen ions by XPS. It was found that at complete core coverage with perovskite shell, the distribution of surface oxygen species according to redox reactivity in CSM resemble pure LSF, but its lattice oxygen storage capacity is 2-2.5 times higher. At partial coverage, the distribution of surface oxygen species according to redox reactivity resembles that in iron oxide.