General Synthesis of Two-Dimensional Porous Metal Oxides/Hydroxides for Microwave Absorbing Applications

Metal oxides/hydroxides with a two-dimensional (2D) porous structure have extensive applications in catalysis, microwave absorption, and energy storage fields due to their large specific surface areas, massive exposed active sites, and good structural integrities. Herein, a general surfactant-assisted vapor diffusion-deposition self-assembly method is developed to synthesize various 2D porous metal oxides/hydroxides. Benefiting from the structure-directing effect of surfactants and the precise tuning of nucleation and growth process that results from this vapor diffusion-deposition strategy, a 2D porous structure is constructed. To explore the advantages of such 2D porous structure, electromagnetic characteristics and absorbing properties of as-obtained materials are investigated. The minimum reflection loss (RL) of 2D porous NiFe₂O₄ is -23.1 dB at 6.4 GHz, and the effective absorption bandwidth (EAB) is 5.1 GHz. However, the minimum RL is only -15.0 dB at 8.7 GHz and the EAB is 3.9 GHz for NiFe₂O₄ particles. In addition, the as-obtained 2D porous NiFe₂O₄ exhibits superior absorbing properties compared with many previously reported nickel ferrites. Furthermore, the microwave absorbing mechanism of 2D porous NiFe₂O₄ is investigated.