One-Step Synthesis of Lignin-Based Triblock Copolymers as High-Temperature and UV-Blocking Thermoplastic Elastomers

This work utilizes frustrated Lewis pairs consisting of tethered bis-organophosphorus superbases and a bulky organoaluminum to furnish the highly efficient synthesis of well-defined triblock copolymers via one-step block copolymerization of lignin-based syringyl methacrylate and n-butyl acrylate, through di-initiation and compounded sequence control. The resulting thermoplastic elastomers (TPEs) exhibit microphase separation and much superior mechanical properties (elongation at break up to 2091 %, tensile strength up to 11.5 MPa, and elastic recovery up to 95 % after 10 cycles) to those of methyl methacrylate-based TPEs. More impressively, lignin-based tri-BCPs can maintain TPEs properties up to 180 °C, exhibit high transparency and nearly 100 % UV shield, suggesting potential applications in temperature-resistant and optical devices.