Ultrasonic pretreatment of spodumene with different size fractions and its influence on flotation

The potential of ultrasonic pretreatment enhancing selective surface dissolution to improve the floatability of spodumene with different size fractions was verified and investigated. For coarse particles of -0.15 + 0.0385 mm, compared with traditional pretreatment methods, ultrasonic pretreatment could optimize the physicochemical properties of the surface, markedly increased the amount of NaOL adsorbed on the mineral surface, and improved the floatability of the spodumene. For fine particles of -0.0385 mm, both pretreatment methods (Ultrasonic and Traditional) could greatly increase the flotation recovery, but ultrasonic pretreatment had no obvious advantage compared with traditional method. ICP combined with XPS analysis were conducted to investigate the dissolution mechanism of spodumene surface in different pretreatment system. Si species on the surface of coarse particles were easily dissolved into the solution under the effect of ultrasound, which increases the relative content of Al and Li species on the surface. This was conducive to the adsorption of the collectors on the surface. However, the selective dissolution of the fine particle surface was weakened by excessive energy intake in the ultrasonic system, which neutralized the advantage brought by the large amount of dissolution, making the results obtained by the two preprocessing methods the same.